Discrete lattice fracture modelling of hydrated cement paste under uniaxial compression at micro-scale
Nengdong Jiang (Shandong University)
Hongzhi Zhang (Shandong University)
Z. Chang (TU Delft - Materials and Environment)
Erik Schlangen (TU Delft - Materials and Environment)
Zhi Ge (Shandong University)
Branko Savija (TU Delft - Materials and Environment)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
A combination of laboratory experiments and numerical simulations at multiple length scales can provide in-depth understanding of fracture behaviour of hydrated cement paste (HCP). To that end, the current work presents a numerical study on compressive failure of hydrated cement paste (HCP) at the micro-scale. Virtual specimens consisting of various phases were obtained using a combination of X-ray computed tomography and image segmentation techniques. The discrete lattice fracture model was used for the deformation and fracture analysis of the specimens subjected to uniaxial compression. The input local mechanical properties of each individual phase were taken from the literature in which a micro-scale compression test was conducted for the calibration of the same type model. The influence of slenderness ratios (1 and 2), water-to-cement ratios (0.3, 0.4 and 0.5 respectively) and lateral confinement of the specimen ends (free and restricted) on the failure behaviour were investigated. It has been shown by the current study that the stress–strain response cannot be completely separated from the used boundary conditions. The proposed model provides an effective tool to understand the compressive fracture behaviour of cement paste at the micro-scale.