Hardening characterisation of a non-proprietary and more eco-friendly UHPC
Ana Matos (Universidade do Porto)
José Granja (Universidade de Coimbra)
Sandra Nunes (Universidade do Porto, TU Delft - Concrete Structures)
José L.Barroso Aguiar (University of Minho)
Miguel Azenha (Universidade de Coimbra)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
The current work provides an integrated analysis of autogenous shrinkage, isothermal calorimetry, and modulus of elasticity measurement through ambient response method (EMM-ARM), to characterise the hardening behaviour of a non-proprietary and more eco-friendly ultra-high performance fibre reinforced cementitious composite (UHPFRC). Isothermal calorimetry revealed that induction period ends at 3 h, and the rapid evolution of hydration heat occurs up to 9 h. Then, the hydration reaction still undergoes but at a very slow rate. The autogenous shrinkage exhibited a strong increase, particularly in the first 6 h, after which a dramatic reduction in the slope of the curves occurred, corroborating with the heat of hydration measurements. The modulus of elasticity evolution pattern revealed a typical cementitious material S-shaped curve, with a strong evolution in the first 8 h and reached 37 GPa at 7 days. As the current study perceives, UHPC/UHPFRC-3 % MOE evolution mainly occurs at very early ages. Thus, using EMM-ARM method for evaluating stiffness-related properties since casting age of UHPC/UHPFRC is of utmost importance to take advantage of the remarkable properties of such advanced material with no waste of time and resources. Furthermore, the UHPFRC developed with a lower amount of cement and silica fume decreases the heat of hydration, shrinkage, and reduced costs and ecological footprint without significantly impairing the MOE, compared to other non-proprietary blended UHPC/UHPFRC mixtures.
help_outline