On the chemo-mechanical evolution process of high-volume slag cement paste
M. Liang (TU Delft - Materials and Environment)
Yu Zhang (TU Delft - Materials and Environment)
S. He (TU Delft - Materials and Environment)
Y. Chen (TU Delft - Materials and Environment)
E. Schlangen (TU Delft - Materials and Environment)
B Savija (TU Delft - Materials and Environment)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
This study investigated the evolution process of high-volume slag cement (HVSC) paste from a chemo-mechanical standpoint. HVSC specimens with a 70 w.t. % slag replacement rate were studied at various ages. Evolution of phase assemblage, microstructure development, and micromechanical properties were analyzed using TGA/XRD/MIP/SEM-EDS and nano-/micro-indentation techniques. A two-scale micromechanical model was built to predict the effective elastic modulus based on the nanoindentation results. Key findings include: 1) Between 7 and 28 days, the formation of calcium silicate hydrate (C-S-H) gel phase improves the effective elastic modulus by filling capillary pores; 2) From 28 to 90 days, the phase assemblage and microstructure remain stable, with a transition from low-density to high-density C-S-H; 3) Between 90 days and 2 years, slag rims produced by slag grains result in increased elastic modulus; 4) The two-scale micromechanical model, combined with nanoindentation data, accurately predicts the effective modulus of HVSC composites, although the unhydrated slag grains-hydrated cement matrix interface may cause an overestimation at an early age. With longer curing time, this interface disappears owing to the continuous hydration of large slag particles and therefore a good match is found between the modelling and experimental results.