A Novel Approach for Controlling the Band Formation in Medium Mn Steels

Journal Article (2018)
Author(s)

H. Farahani (TU Delft - Novel Aerospace Materials)

W. Xu (Northeastern University China)

Sybrand Van Der Zwaag (TU Delft - Novel Aerospace Materials)

Research Group
Novel Aerospace Materials
Copyright
© 2018 H. Farahani, W. Xu, S. van der Zwaag
DOI related publication
https://doi.org/10.1007/s11661-018-4565-8
More Info
expand_more
Publication Year
2018
Language
English
Copyright
© 2018 H. Farahani, W. Xu, S. van der Zwaag
Research Group
Novel Aerospace Materials
Bibliographical Note
green@en
Issue number
6
Volume number
49
Pages (from-to)
1998–2010
Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Abstract

Formation of the microstructural ferrite/pearlite bands in medium Mn steels is an undesirable phenomenon commonly addressed through fast cooling treatments. In this study, a novel approach using the cyclic partial phase transformation concept is applied successfully to prevent microstructural band formation in a micro-chemically banded Fe-C-Mn-Si steel. The effectiveness of the new approach is assessed using the ASTM E1268-01 standard. The cyclic intercritical treatments lead to formation of isotropic microstructures even for cooling rates far below the critical one determined in conventional continuous cooling. In contrast, isothermal intercritical experiments have no effect on the critical cooling rate to suppress microstructural band formation. The origin of the suppression of band formation either by means of fast cooling or a cyclic partial phase transformation is investigated in detail. Theoretical modeling and microstructural observations confirm that band formation is suppressed only if the intercritical annealing treatment leads to partial reversion of the austenite-ferrite interfaces. The resulting interfacial Mn enrichment is responsible for suppression of the band formation upon final cooling at low cooling rates.