Efficient hydrogen storage in defective graphene and its mechanical stability
A combined density functional theory and molecular dynamics simulation study
G.K. Sunnardianto (TU Delft - (OLD) MSE-7, Indonesian Institute of Sciences (LIPI))
George Bokas (Université Catholique de Louvain)
Abdelrahman Hussein (TU Delft - Ship Hydromechanics and Structures)
C.L. Walters (TU Delft - Ship Hydromechanics and Structures)
Othonas A. Moultos (TU Delft - Engineering Thermodynamics)
Poulumi Dey (TU Delft - Team Poulumi Dey)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
A combined density functional theory and molecular dynamics approach is employed to study modifications of graphene at atomistic level for better H2 storage. The study reveals H2 desorption from hydrogenated defective graphene structure, V222, to be exothermic. H2 adsorption and desorption processes are found to be more reversible for V222 as compared to pristine graphene. Our study shows that V222 undergoes brittle fracture under tensile loading similar to the case of pristine graphene. The tensile strength of V222 shows slight reduction with respect to their pristine counterpart, which is attributed to the transition of sp2 to sp3-like hybridization. The study also shows that the V222 structure is mechanically more stable than the defective graphene structure without chemically adsorbed hydrogen atoms. The current fundamental study, thus, reveals the efficient recovery mechanism of adsorbed hydrogen from V222 and paves the way for the engineering of structural defects in graphene for H2 storage.