Print Email Facebook Twitter Analysis of Stochastic Matrix Crack Evolution in CFRP Cross-Ply Laminates under Fatigue Loading Title Analysis of Stochastic Matrix Crack Evolution in CFRP Cross-Ply Laminates under Fatigue Loading Author Li, X. (TU Delft Structural Integrity & Composites; Center of Excellence in Artificial Intelligence for Structures) Benedictus, R. (TU Delft Structural Integrity & Composites) Zarouchas, D. (TU Delft Structural Integrity & Composites; Center of Excellence in Artificial Intelligence for Structures) Date 2023 Abstract The present work aims at understanding the stochastic matrix crack evolution in CFRP cross-ply laminates under tension–tension fatigue loading. An experimental campaign was carried out on twenty-three specimens at different stress levels, while two optical techniques were used for the in-situ monitoring of the accumulation of transverse matrix cracks. The results showed a significant scatter in crack evolution among specimens. This stochastic behaviour was further investigated using image analysis and numerical modelling. It was found that transverse matrix cracks can be classified into the independent and dependent cracks based on a critical crack spacing. Furthermore, the severity of interaction among cracks was quantified by introducing a dependent crack ratio. Finally, a strength-based probabilistic model was proposed to describe the scattering regime of the crack evolution. The agreement between model and test results indicates that local strength variations of 90 plies are the dominant scattering source governing the initial fatigue resistance to cracking and determining the accumulation of transverse matrix cracks among specimens. These results may provide a new insight into the stochastic nature of matrix cracking in composite laminates and aid in the design of fatigue resistance properties. Subject Composite laminatesFatigueIn-situ damage monitoringPhenomenological model To reference this document use: http://resolver.tudelft.nl/uuid:f17718be-e3cf-4bd0-aa1b-4ad057e06906 DOI https://doi.org/10.1016/j.engfailanal.2023.107277 ISSN 1350-6307 Source Engineering Failure Analysis, 150 Part of collection Institutional Repository Document type journal article Rights © 2023 X. Li, R. Benedictus, D. Zarouchas Files PDF 1_s2.0_S1350630723002315_main.pdf 7.17 MB Close viewer /islandora/object/uuid:f17718be-e3cf-4bd0-aa1b-4ad057e06906/datastream/OBJ/view