Title
Effect of microstructure induced anisotropy on fatigue behaviour of functionally graded Inconel 718 fabricated by additive manufacturing
Author
Ghorbanpour, S. (TU Delft Team Vera Popovich) 
Sahu, Saswat (Student TU Delft)
Deshmukh, Kaustubh (Student TU Delft)
Borisov, Evgenii (Peter the Great Saint-Petersburg Polytechnic University)
Riemslag, A.C. (TU Delft Team Vera Popovich)
Reinton, T.E. (TU Delft Team Vera Popovich)
Morete Barbosa Bertolo, V. (TU Delft Team Vera Popovich)
Jiang, Quanxin (TU Delft Team Vera Popovich)
Popovich, Anatolii (Peter the Great Saint-Petersburg Polytechnic University)
Shamshurin, Aleksey (Peter the Great Saint-Petersburg Polytechnic University)
Knezevic, Marko (University of New Hampshire Durham)
Popovich, V. (TU Delft Team Vera Popovich; Peter the Great Saint-Petersburg Polytechnic University)
Date
2021
Abstract
In this paper, the effect of microstructural anisotropy on the fatigue crack growth behaviour of the functionally graded Inconel 718 fabricated through laser powder bed fusion (L-PBF) is investigated. Different manufacturing parameters, including low and high laser powers, were used to produce a variety of non-graded (NG) and functionally graded (G) specimens in two build directions, vertical and horizontal. In addition, a group of heat treated wrought samples was tested as a reference. It was observed that the different manufacturing parameters result in various grain size, crystallographic textures, precipitates and Laves phases, porosity, and un-melted particles. Three-point bending fatigue tests were conducted to measure the threshold stress intensity factor (ΔKth) and fatigue crack growth rate (FCGR),da/dN. Only the lower laser power L-BPF Inconel material was found to have comparable to the wrought heat treated material fatigue crack growth behaviour. Furthermore, a new approach of automatically controlling ΔK as a function of the crack length was employed for graded specimens to investigate the crack growth rate as a function of local microstructure. The FCGR value of the vertical L-PBF samples, in which the crack direction was perpendicular to the build direction, remained constant. In contrast, the da/dN value of the horizontal samples with the crack direction parallel to the build direction increased constantly with the increase of the crack length. This behaviour is in good agreement with the hardness profile of the graded materials. Melt pool boundaries, graded interface boundaries, and grain orientations close to 〈001〉 were found to deflect the crack path. Additionally, it was found that L-PBF material is more affected (at a low stress ratio of R = 0.1) by the roughness-induced crack closure than the wrought counterparts. This study has successfully demonstrated the feasibility of using an additive manufacturing process to fabricate functionally graded materials featuring tailorable fatigue response of the local microstructures.
Subject
Fatigue behaviour
Functionally graded materials
Inconel 718
Laser powder bed fusion
Microstructural anisotropy
To reference this document use:
http://resolver.tudelft.nl/uuid:c8a836d6-6624-4438-ba6c-fea23ce8c119
DOI
https://doi.org/10.1016/j.matchar.2021.111350
ISSN
1044-5803
Source
Materials Characterization, 179
Part of collection
Institutional Repository
Document type
journal article
Rights
© 2021 S. Ghorbanpour, Saswat Sahu, Kaustubh Deshmukh, Evgenii Borisov, A.C. Riemslag, T.E. Reinton, V. Morete Barbosa Bertolo, Quanxin Jiang, Anatolii Popovich, Aleksey Shamshurin, Marko Knezevic, V. Popovich