- document
-
Schijve, J. (author), Jacobs, F.A. (author), Tromp, P.J. (author)Tests were carried out on open-hole specimens, lugs and riveted strap joints of 2024-T3 and 7075-T6 materials. The effects of design stress level, truncating high-amplitude gust loads and omitting low-amplitude gust cycles were stuaied. Observations of the open-hole specimens include data on crack initiation, crack closure and damage increments....report 1974
- document
-
van Leeuwen, H.P. (author), Schra, L. (author)Material from forgings rejected after cracking in service was given a variety of heat treatments. Material aged to peak hardness was susceptible to SCC at all ageing temperatures. Overageing at temperatures around 160° C imparted a significant increase in SCC resistance while useful strength was retained. An additional one week ageing at 160° C...report 1973
- document
- Schijve, J. (author) report 1972