Investigation of mode-II delamination fracture energy with a discontinuous computational homogenization model

Numerical methods for delamination analysis, such as the cohesive zone method, require fracture energy as an essential input. Existing formulations rely on a phenomenological relationship that links fracture energy to the mode of fracture based on linear elastic fracture mechanics (LEFM). However, doubts exist about the applicability of LEFM....

Simulation of cusp formation in composite materials using the thick level set method

On the microlevel, cusps are formed during delamination crack growth under mode II loading conditions. In this work, the Thick Level Set (TLS) approach is used to simulate the cusp formation process. A plasticity model for polymers is implemented in the TLS method and a new loading scheme is devised to deal with permanent strain. A numerical...

Cohesive zone and level set method for simulation of high cycle fatigue delamination in composite materials

This paper deals with high cycle fatigue delamination in composite materials. The cohesive zone approach along with the level set method is used to simulate fatigue-driven delamination growth. The cohesive zone method is used for calculation of the energy release rate at the crack front because of its superiority over the virtual crack...

The Transverse Crack Tension test revisited: An experimental and numerical study

Several problems arise when measuring the mode II interlaminar fracture toughness using a Transverse Crack Tension specimen; in particular, the fracture toughness depends on the geometry of the specimen and cannot be considered a material parameter. A preliminary experimental campaign was conducted on TCTs of different sizes but no fracture...

Modeling fatigue-driving delamination using a thick level set interface model

This paper presents a new discontinuous damage model for simulating fatigue-driven delamination in composites. Fatigue models commonly describe crack growth using the Paris law which provides the link between the energy released due to delamination and the crack growth rate. A core issue in implementing the Paris law is to accurately compute the...