Microbially mediated carbonation of marine alkaline minerals: Potential for concrete crack healing

Concrete constructions in the marine environment suffer from chemical attack of sea salts which can induce damage to both the concrete matrix and embedded steel reinforcement. For example, ingress of sulfate and chloride ions can respectively result in detrimental ettringite formation and enhanced corrosion of the steel rebars. The first...

Microbially mediated carbonation of marine alkaline minerals: Potential for concrete crack healing

Concrete constructions in the marine environment suffer from chemical attack of sea salts which can induce damage to both the concrete matrix and embedded steel reinforcement. For example, ingress of sulfate and chloride ions can respectively result in detrimental ettringite formation and enhanced corrosion of the steel rebars. The first...

Durability of Marine Concrete under Thermal Cycling Loads

Data on chloride penetration into concrete exposed to a simulated aggressive marine environment are presented. Concrete specimens, large beams and small cubes, are subjected to 90 complete exposure cycles of wetting and drying plus heating and cooling. The applied exposure condition consists of a drying period of 42 hrs followed by a wetting...