Influence of environments on constant displacement stress corrosion crack growth in high strength aluminium alloys

An experimental investigation was carried out into the applicability of various corrosive environments for stress corrosion crack propagation testing of high strength aluminium alloys using double cantilever beam specimens. Testing under atmospheric conditions was used as a reference. It was found that stress corrosion crack growth under...

The effect of sheet thickness and laminating on the fatigue resistance of the aluminium alloyd AL-7010T73651

The influence of sheet thickness (2 mm and 10 mm) and the influence of laminating (5x2 ram) on the fatigue crack growth properties of the aluminium alloy AL 7010-T 73651 were investigated. Both constant amplitude loading and flight simulation loading were applied. All 2 mm and 10 mm thick sheets were machined from a 150 mm thick plate, i.e....