Heat treatment studies of aluminium alloy type 7050 forgings. Interim report no. 3: Corroded-specimen fatigue tests and SCC propagation tests

The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...

Effects of crack plane orientation transitions on flight simulation fatigue crack propagation in a high strength aluminium alloy (7050)

The effects of flat to slant fracture transitions on flight simulation fatigue crack propagation in specimens of 7O5O aluminium alloy forgings are discussed. For specimens containing flat, shearlipped, or full slant fractures at similar crack lengths the crack resistance (R curve) approach appears to provide an explanation for differences in the...