Modeling of microstructural effects on the creep of hardened cement paste using an experimentally informed lattice model

This paper presents a method to numerically investigate the microstructural effect on the creep behavior of cement paste at the microscale. The lattice fracture model is extended to consider local time-dependent deformations of calcium-silicate-hydrate phases in the cement paste by imposing local forces. The term “experimentally informed...

Assessing strain rate sensitivity of cement paste at the micro-scale through micro-cantilever testing

This study presents an experimental investigation of the rate-dependent mechanical properties of cement paste at the microscale. With the use of a nanoindenter, micro-cantilever beams with the size of 300 μm × 300 μm × 1650 μm were loaded at five different strain rates from around 10⁻⁶/s to 10⁻²/s until failure. It is...

Fundamental investigation on the frost resistance of mortar with microencapsulated phase change materials

Recent studies have shown that concrete containing Phase Change Materials (PCM) with low transition temperatures may reduce the number of freeze/thaw cycles suffered by the cementitious composite in temperate climates. Nevertheless, the positive influence of such admixtures on the frost resistance of cement-based materials has not been...

Elucidating the effect of accelerated carbonation on porosity and mechanical properties of hydrated Portland cement paste using X-ray tomography and advanced micromechanical testing

Carbonation of hydrated cement paste (HCP) causes numerous chemo-mechanical changes in the microstructure, e.g., porosity, strength, elastic modulus, and permeability, which have a significant influence on the durability of concrete structures. Due to its complexity, much is still not understood about the process of carbonation of HCP. The...

Chemo-physico-mechanical properties of the interface zone between bacterial PLA self-healing capsules and cement paste

In this study, the interface between different types of bacteria-embedded self-healing polylactic acid capsules (PLA) and cement paste is investigated. Particularly, the changes in microstructure and mechanical properties of the interface with respect to bulk cement paste were studied. First, nanoindentation was performed to obtain maps of...

Numerical investigation of crack self-sealing in cement-based composites with superabsorbent polymers

Recently the concept of crack self-sealing has been investigated as a method to prevent degradation and/or loss of functionality of cracked concrete elements. To obtain self-sealing effect in the crack, water swelling admixtures such as superabsorbent polymers (SAP) are added into the cementitious mix. In order to design such self-sealing...