- document
-
Lameris, J. (author)In the full scale durability and damage tolerance tests of composite aircraft structures, the US and European certification requirements demand among other things that the number of cycles applied are statistically significant and that the influence of the environment has been taken into account. Several certification methods are described which...report 1990
- document
-
Wanhill, R.J.H. (author)Flight simulation fatigue crack propagation tests with gust spectrum loading were carried out on 2024-T3/carbon-epoxy, 7475-T76l/carbon-epoxy and Ti-6Al-4V/carbon-epoxy laminates with nominal weight savings of -30% as compared to equivalent 2024-T3 panels. The performance of the 2024-T3/carbon-epoxy laminates was much superior to those of the...report 1978
- document
-
de Jonge, J.B. (author), Nederveen, A. (author), Tromp, P.J. (author)Fatigue tests under flight simulation loading were done on simple notched 2024-T3 Alclad sheet specimens. Reduction of the gust load amplitudes resulted in an increase of crack initiation life but hardly influenced crack propagation. Reduction of the overall stress level increased both initiation and crack propagation life. The observed...report 1978
- document
-
Wanhill, R.J.H. (author)Flight simulation fatigu-e crack propagation tests were carried out on 2024-T3, 7475-T761 and mill annealed Ti-6A1-4V sheet in thicknesses up to 3 miri and representative for transport aircraft lower wing skin stiffened panels of end load capacities 1.5 and 3 MN/m. The performance of 2024-T3 was much superior, owing mainly to greater retardation...report 1977