Fatigue damage in composites under different loading conditions

The damage development In notched (± 45, 0„, 90, 0-) carbon-epoxy coupon specimens tested under different loading conditions was determined. Constant amplitude tests at R = -1 and R = 0.1 as well as flight simulation tests were performed to establish those stress values for which no damage growth occurs.

The effect of impact damage on the tension-compression fatigue properties of sandwich panels with face sheets of carbon epoxy

An experimental investigation was performed to examine the effect of low energy impact damage on tension-compression fatigue properties of sandwich panels. The specimens consisted of a 9 mm thick Nomex honeycomb and face sheets of (0,± 45) and (± 45,0) Carbon/epoxy. Drop weight impact was applied to create internal laminate damage. In order to...