Heat treatment studies of aluminium alloy forgings of the AZ 74.61 type. Interim report no. 3: Fatigue crack propagation performance under manoeuvre spectrum loading

The fatigue crack propagation performance of the alloy AZ 74.61 under manoeuvre spectrum loading was studied. The crack propagation behaviour was also compared with that of the American forging alloy AA 7050, not only for simulated manoeuvre loading but also for simulated gust loading and programme loading. It was found that, at comparable...

Heat treatment studies of aluminium alloy type 7050 forgings. Interim report no. 2: The effect of heat treatment on a variety of engineering properties

The effect of variety of heat treatments on various engineering properties was studied with the aim to derive an optimum heat treatment. The engineering properties comprised Vickers hardness, short-time tensile strength, fatigue crack propagation resistance, fracture toughness and stress corrosion resistance. The test results were compared with...

Rate effects on residual strength of flawed structures and materials

The literature is reviewed with respect to: - tests conducted to investigate crack re-initiation under dynamic load and arrest of a running crack - metallurgical sources of rate effects - available data for aerospace engineering materials - mechanical sources of rate effects, i.e. dynamic crack tip stresses and kinetic energy effects Conclusions...

Heat treatment and SCC susceptibility of AU4SG type forged material

Material from forgings rejected after cracking in service was given a variety of heat treatments. Material aged to peak hardness was susceptible to SCC at all ageing temperatures. Overageing at temperatures around 160° C imparted a significant increase in SCC resistance while useful strength was retained. An additional one week ageing at 160° C...