Stress corrosion resistance of damage tolerant aluminium-lithium sheet materials

The SCC resistances of three damage tolerant aluminium sheet materials were determined by means of the ASCOR (Automated Stress COrrosion Ring) test. The conventional damage tolerant sheet material 2024-T3 was used as reference. The SCC resistance of 8090-T81 turned out to be only slightly lower than the SCC resistance of 2024-T3. In contrast,...

Outdoor corrosion testing of aluminium-lithium alloys

Outdoor corrosion and stress corrosion tests were conducted on Al-Li plate and sheet materials for 3 and almost 5 years respectively. The results can be summarized as follows: Corrosion: Peak aged XXXA-T651 (8090-T651) exhibited greater exfoliation corrosion resistance than 2024-T351 and 2324-T39 plate. 2091-T3 and 2024-T3 sheet were found to be...

Effects of cooling rate on corrosion properties of high strength aluminium alloys under atmospheric conditions

Long-term outdoor exposure tests were done to investigate the effect of cooling rate on corrosion and stress corrosion properties of extruded rods of the high strength aluminium alloys 2024-T4, 2023-T6, 7075-T6 and 7075-T73. The 2024 alloy exhibited a high susceptibility to SCC irrespective of best treatment and cooling rate, whereas 7075-T6 was...

Flight simulation environmental fatigue crack propagation in 2024-T3 and 7475-T761 aluminium

Flight simulation fatigue crack propagation tests on 202U-T3 and 7475-T761 aluminum alloy sheet were carried out using a gust spectrum representative of the load history of an under wing skin in a transport aircraft. The investigation included tests at several design stress levels and in environments of laboratory air and air plus water spray....

Testing of coatings and materials for jet engine components in simulated operational environments

Military aircraft flying low level missions in Western Europe encounter a very different environment from that in most of the United States. Industrial pullution causes atmospheric moisture to be highly acid, and the corrosion rate of jet engine components is greatly increased, with consequent high maintenance costs. To help combat this problem...

Heat treatment studies of aluminium alloy forgings of the AZ 74.61 type. Interim report no. 3: Fatigue crack propagation performance under manoeuvre spectrum loading

The fatigue crack propagation performance of the alloy AZ 74.61 under manoeuvre spectrum loading was studied. The crack propagation behaviour was also compared with that of the American forging alloy AA 7050, not only for simulated manoeuvre loading but also for simulated gust loading and programme loading. It was found that, at comparable...