The effect of fatigue crack length on the residual strength of ARALL3 panels with fingertip doublers

Fatigue and residual strength tests were done on doubler specimens consisting of an ARALL3 (3/2) laminate with a bonded-on fingertip doubler. The primary objective was to determine the effect of fatigue crack length on the residual strenght and delamination onset stress for this type of specimen. The specimens were precracked to variable crack...

Effect of penetrant on fatigue of aluminium alloy lap joints

The effect of penetrant on the fatigue life of single shear riveted lap joints was investigated by flight simulation fatigue tests using the MINITWIST gust spectrum. The penetrant/material combination investigated was ARDROX 985 P3T and aluminium alloy 202U-T3 sheet material (both bare and clad) respectively. The effect of penetrant on the...

Engineering property comparisons of PM alloy X7091-T7E69 and IM alloy forgings

The engineering properties of PM alloy X7091-T7E69 forgings were compared with those of forgings of the IM alloys 7075-T73, 7175-T736, 7050-T736 and 7010-T736. The properties considered were: strength, fracture toughness, fatigue crack propagation under constant amplitude and flight simulation loading, stress corrosion crack initiation and...

The tail of the test spectrum: The effect of different approximations of the lower end of a gust load spectrum on crack growth and fatigue life in 7075-T6 and 2024-T3 specimens

The influence of the approximation of the lower end of the load spectrum was investigated by comparative tests using the Basic F-27 test programme and an extended version, containing three times more cycles per flight. Crack growth was studied on notched sheet specimens made of Alclad 202U-T3 and Alclad TOT5-T6. Fatigue life tests were done on...

The effect of sheet thickness and laminating on the fatigue resistance of the aluminium alloyd AL-7010T73651

The influence of sheet thickness (2 mm and 10 mm) and the influence of laminating (5x2 ram) on the fatigue crack growth properties of the aluminium alloy AL 7010-T 73651 were investigated. Both constant amplitude loading and flight simulation loading were applied. All 2 mm and 10 mm thick sheets were machined from a 150 mm thick plate, i.e....

Engineering properties of the recently developed aluminium alloy designated 7010

An experimental investigation.was performed on 80 mm thick plate material of 7OIO-T7651 and 7OIO-T73651 developed by Alcan Industries Ltd in U.K. The testing programme involved: tensile tests, fracture toughness, stress corrosion and fatigue tests. For comparison a similar investigation vas carried out on 7075-T7351 Alcoa plate material.