Engineering property comparisons for 2324-T39 and 2024-T351 aluminium alloy plate

Engineering property comparisons have been made for plate material of the newly developed aluminium alloy 2324-T39 and the widely used alloy 2024-T351. The properties considered were: tensile strength, fracture toughness, notched fatigue strength, and the resistance to fatigue crack propagation under both constant amplitude and flight simulation...

Some tests to assess the effect of crack stoppers on the fatigue life of centre-notched sheetspecimens

Several simple crack stopping methods were evaluated In fatigue crack propagation tests on 2024-T3 Alclad sheet specimens. After precracklng until a crack of 40 mm was obtained crack stoppers were Installed and the fatigue test was continued. Crack stoppers Installed In stop holes were: a blind rivet, a hard driven rivet, a heavily tightened...

The use of standardized fatigue load sequences in coupon and component tests

Due to the development of servo hydraulic fatigue testing machines, fatigue tests under realistic loading conditions have become possible. In these tests, standardized load sequences can be applied. The paper describes the main properties of such sequences, including TWIST and FALSTAFF. Various examples of application of these sequences are...

Manoeuvre spectrum fatigue crack propagation in aluminium alloy sheet materials

2024-T3, 2048-T851, 7075-T6 and 7475-T761 aluminium alloy sheets were compared for fatigue crack propagation resistance under manoeuvre spectrum and constant amplitude loading. For manoeuvre spectrum loading 7475-T761 was superior overall, and this superiority is most probably due to superior toughness of this alloy. In more detail, 2024-T3 was...

The effect of sheet edge working on the fatigue life under flight-simulation loading

Fatigue tests under flight-simulation loading have been performed on unnotched Alclad 2024-T3, anodised 2.0 mm thick sheet specimens, manufactured according to several machine-shop processes applied in the air craft industry. From the results it appears that milling is preferable to stamping. Rounding off the edges is also advantageous. The...

Environmental effects on crack grwoth in flight-simulation tests on 2024-T3 and 7075-T6 material Supplement: Compilation of test data from an investigation on the effect of environment on crack growth under flight-simulation loading

Flight-simulation tests based on a standardized gust load spectrum were carried out in normal air, very dry air and salt water. Specimen thicknesses were t = 2 mm and t = 10 mm, mean stress in flight was 70 or 55 MN/m². In all cases a significant effect of the environment was found. Fatigue lives for t = 10 ram were much shorter than for t = 2...

Fracture toughness and fatigue properties of the new aluminium alloy 7475-T76

Residual strength tests have been performed on 610 mm wide centre cracked panels. During the tests, stable crack growth was filmed and crack opening displacements were measured. Fracture toughness was determined using the method of Feddersen. Flight simulation fatigue tests were carried out to investigate the crack propagation properties. A...