Oldersma, A. (author), Wanhill, R.J.H. (author)Discussions between D-BAA and the NLR have shown that significant variability in fatigue crack growth properties is possible for the industry standard damage tolerant aluminium alloy, 2024-T3 sheet. This is important for two reasons: (1) design assumptions and (2) comparisons of different candidate materials, such as 6013-T6, with 2024-T3....report 1996
- document
-
Kolkman, H.J. (author)Differences in the fatigue crack propagation rates of 2024-T351 and 2324-T39 are explicable from differences in microstructures. The slope changes (transitions) in the crack propagation curves are probably associated with the plastic zone sizes being equal to certain microstructural dimensions. As a consequence of different chemical compostion...report 1985
- document
-
Schijve, J. (author), Jacons, F.A. (author), Meulman, A.E. (author)Flight simulation tests on 2024-T3 and 7075-T6 lug specimens indicated significant fatigue life improvements obtained by expanding the holes in accordance with the split-sleeve cold work method. Geometrical distortions induced by the expansion were measured. The significance of residual stresses is analysed with reference to depth of penetration...report 1978
- document
-
Wanhill, R.J.H. (author)2024-T3, 2048-T851, 7075-T6 and 7475-T761 aluminium alloy sheets were compared for fatigue crack propagation resistance under manoeuvre spectrum and constant amplitude loading. For manoeuvre spectrum loading 7475-T761 was superior overall, and this superiority is most probably due to superior toughness of this alloy. In more detail, 2024-T3 was...report 1978
- document
-
Schra, L. (author), van Leeuwen, H.P. (author), Meulman, A.E. (author)The fatigue crack propagation performance of the alloy AZ 74.61 under manoeuvre spectrum loading was studied. The crack propagation behaviour was also compared with that of the American forging alloy AA 7050, not only for simulated manoeuvre loading but also for simulated gust loading and programme loading. It was found that, at comparable...report 1976
- document
-
't Hart, W.G.J. (author), Nederveen, A. (author), Stoffels, E. (author), Tromp, J. (author)Residual strength tests have been performed on 610 mm wide centre cracked panels. During the tests, stable crack growth was filmed and crack opening displacements were measured. Fracture toughness was determined using the method of Feddersen. Flight simulation fatigue tests were carried out to investigate the crack propagation properties. A...report 1975