Stress corrosion resistance of damage tolerant aluminium-lithium sheet materials

The SCC resistances of three damage tolerant aluminium sheet materials were determined by means of the ASCOR (Automated Stress COrrosion Ring) test. The conventional damage tolerant sheet material 2024-T3 was used as reference. The SCC resistance of 8090-T81 turned out to be only slightly lower than the SCC resistance of 2024-T3. In contrast,...

Heat treatment studies of aluminium alloy type 7050 forgings. Interim report no. 3: Corroded-specimen fatigue tests and SCC propagation tests

The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...

Rate effects on residual strength of flawed structures and materials

The literature is reviewed with respect to: - tests conducted to investigate crack re-initiation under dynamic load and arrest of a running crack - metallurgical sources of rate effects - available data for aerospace engineering materials - mechanical sources of rate effects, i.e. dynamic crack tip stresses and kinetic energy effects Conclusions...