- document
-
Wanhill, R.J.H. (author)Archaeological silver may be embrittled by long-term corrosion and microstructural changes. The embrittlement of artifacts increases with increasing grain size. This is explained by considering the grain boundary character and models describing the interactions between microcracks, lattice dislocations and grain boundaries. Severely embrittled...report 2001
- document
-
Wanhill, R.J.H. (author), Schra, L. (author), 't Hart, W.G.J. (author)New impetus to continued use of alximinium alloys in major structural areas of aircraft has been given by the development of aluminium-lithium alloys. However, qualification of these new materials for service requires extensive testing and evaluation, preferably in international cooperative programmes. The evaluation of aluminium-lithium alloys...report 1989
- document
-
de Graaf, E.A.B. (author), de Rijk, P. (author)The present report describes how fatigue cracks were produced in 102 specimens. After cracking these specimens were inspected non-destructively by means of eddy currents, ultrasonics. X-rays and penetrants, and the indications were recorded. Successively the specimens were exposed to corrosion whereafter the inspections were repeated. Upon...report 1978
- document
-
Schra, L. (author), van Leeuwen, H.P. (author)The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...report 1977
- document
-
Schijve, J. (author), Jacobs, F.A. (author), Tromp, P.J. (author)Flight-simulation tests were carried out on sheet specimens notched "by an open hole (Kt = 2.66). The material was 2024-T3 in three conditions; Alclad, bare and chemically milled. The crack initiation period and the crack propagation period were considerably shorter for the Alclad material. The significance of the cladding, both for constant...report 1976