Heat treatment studies of aluminium alloy type 7050 forgings. Interim report no. 3: Corroded-specimen fatigue tests and SCC propagation tests

The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...

The significance of cladding for fatigue of aluminium alloys in aircraft structures

Flight-simulation tests were carried out on sheet specimens notched "by an open hole (Kt = 2.66). The material was 2024-T3 in three conditions; Alclad, bare and chemically milled. The crack initiation period and the crack propagation period were considerably shorter for the Alclad material. The significance of the cladding, both for constant...