A study of the elastic moduli and chemical composition of corrosion product naturally-generated due to chlorides through nano-indentation and energy dispersive X-ray spectrometry (EDS)

An important input parameter for numerical models that simulate cracking of the concrete cover due to reinforcement corrosion is the Elastic modulus of corrosion product (Ecp). Despite its relevance, Ecp is subject of significant variations according to the values reported in the literature, which vary from less than 100 MPa up to 360 GPa....

A study of the elastic moduli and chemical composition of corrosion product naturally-generated due to chlorides through nano-indentation and energy dispersive X-ray spectrometry (EDS)

An important input parameter for numerical models that simulate cracking of the concrete cover due to reinforcement corrosion is the Elastic modulus of corrosion product (Ecp). Despite its relevance, Ecp is subject of significant variations according to the values reported in the literature, which vary from less than 100 MPa up to 360 GPa....

Analysis of naturally-generated corrosion products due to chlorides in 20-year old reinforced concrete: An elastic modulus-mineralogy characterization

The elastic modulus of corrosion product (E_cp) has been reported with significant variations in the literature. This study aims to investigate the E_cp of naturally-generated chloride-induced corrosion products formed in different concrete mixes. Microstructural characterization was conducted through nano-indentation,...

The influence of defects at the steel/concrete interface for chloride-induced pitting corrosion of naturally-deteriorated 20-years-old specimens studied through X-ray Computed Tomography

Although reinforcement corrosion is a well-known issue, which are the locations of the steel/concrete interface most sensitive to pitting corrosion is still an unclear issue. In this study, X-ray computed tomography is used to characterize eight 20-years-old reinforced concrete cores naturally deteriorated due to chloride-induced corrosion....

The influence of defects at the steel/concrete interface for pitting corrosion initiation studied through X-ray Computed Tomography and image analysis

Although corrosion of reinforcement is a well-known issue for the construction industry, there are still open questions about some fundamentals of corrosion in reinforced concrete. These points include, among others, which are the most sensitive locations of the steel/concrete interface for pitting corrosion to initiate and to propagate. In...