A test plan for sustained load fracture control verification

An example test plan for sustained load fracture control verification is presented. Two sustained load fracture problems have been chosen: stress corrosion cracking of titanium alloy Ti-6Al-4V, and gaseous hydrogen embrittlement of the nickel-base superalloy Inconel 718. The plan is worked out in detail, including materials and heat treatments,...

Spacecraft sustained load fracture control

The opportunities for sustained load fracture control in spacecraft are indicated. Emphasis is given to verification by small-scale laboratory testing.

Corrosion fatigue crack arrest in aluminium alloys

The economic life of airframes is largely determined by widespread initiation and growth of fatigue cracks at low stress intensities. Any factor reducing the low stress intensity fatigue damage rate could, if controllable, increase the structural durability. One such factor is corrosion fatigue crack arrest. Corrosion product build-up within a...

Hydrogen embrittlement 0f 4340 steel by cadmium electroplating; interim report no. 1.