The effect of pH on the corrosion protection of aluminum alloys in lithium-carbonate-containing NaCl solutions

The corrosion inhibiting effect of lithium carbonate has been studied over the pH range relevant for atmospheric corrosion conditions at the polymer/metal interface. It is demonstrated that lithium carbonate offers optimum corrosion protection under moderately alkaline conditions attributed to the formation of a protective layer identified as...

Passive film formation and corrosion resistance of laser-powder bed fusion fabricated NiTi shape memory alloys

Electrochemical tests and surface analysis measurements were performed to study the corrosion behavior in a 0.9 wt.% NaCl solution at 37 °C of three NiTi shape memory alloys fabricated by laser-powder bed fusion (L-PBF). The passive film characteristics and corrosion resistance of L-PBF NiTi showed different features as a function of their...

Laterally-resolved formation mechanism of a lithium-based conversion layer at the matrix and intermetallic particles in aerospace aluminium alloys

Lithium leaching coatings have recently been developed as eco-friendly active corrosion protection technology for aerospace aluminium alloys (AAs) by the formation of a conversion layer at coating defects. While general conversion layer formation characteristics were studied and reported before, here we study the local layer formation process...

Nanorods grown by copper anodizing in sodium carbonate

Self-organized anodization of copper in 0.1 M Na2CO3 electrolyte was studied in order to obtain nanostructured oxide surface on the metal substrate. Linear sweep voltammetry (LSV) revealed that the most suitable voltage range for anodic film formation is from 3 to 31 V. In this range (except between 3 and 7 V), the oxide is formed as nanorods,...

Morphology and photoluminescence of nanostructured oxides grown by copper passivation in aqueous potassium hydroxide solution

Copper foil was anodized in 1 M KOH at potentials ranging from −400 to −100 mV vs. Ag|AgCl electrode. Cyclic voltammetry showed a distinct peak with a maximum at around −150 mV. For anodizing at −100 and −200 mV, nanowires with diameters of ca. 19 and 24 nm respectively were found to be grown. Moreover, photoluminescence and X-ray diffraction...