Schra, L. (author)An interlaboratory testing programme to evaluate the rising displacement test for stress corrosion crack (SCO growth investigations was carried out within the framework of the "Measurements and Testing" programme of the European Community under BCR contract nr. MATI CT 930038. The contribution of the NLR to the project consisted of testing of...report 1996
- document
-
Schra, L. (author), 't Hart, W.G.J. (author), Boogers, J.A.M. (author)Outdoor corrosion and stress corrosion tests were conducted on Al-Li plate and sheet materials for 3 and almost 5 years respectively. The results can be summarized as follows: Corrosion: Peak aged XXXA-T651 (8090-T651) exhibited greater exfoliation corrosion resistance than 2024-T351 and 2324-T39 plate. 2091-T3 and 2024-T3 sheet were found to be...report 1990
- document
-
Schra, L. (author), van Leeuwen, H.P. (author)The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...report 1977