Damage tolerance property comparisons for 2000 and 8000 series aluminium plate alloys

This report compares the mechanical properties, fracture toughness and fatigue crack growth properties of the damage tolerant/medium strength aluminium plate alloys 2024-T351, 2324-T39, 8090-T651 and 8090-T8171. The main objective, in view of previous work, was to determine whether damage tolerant 8090-T8171 plate can advantageously replace the...

Influence of environments on constant displacement stress corrosion crack growth in high strength aluminium alloys

An experimental investigation was carried out into the applicability of various corrosive environments for stress corrosion crack propagation testing of high strength aluminium alloys using double cantilever beam specimens. Testing under atmospheric conditions was used as a reference. It was found that stress corrosion crack growth under...

The effect of sheet thickness and laminating on the fatigue resistance of the aluminium alloyd AL-7010T73651

The influence of sheet thickness (2 mm and 10 mm) and the influence of laminating (5x2 ram) on the fatigue crack growth properties of the aluminium alloy AL 7010-T 73651 were investigated. Both constant amplitude loading and flight simulation loading were applied. All 2 mm and 10 mm thick sheets were machined from a 150 mm thick plate, i.e....

Engineering property comparisons of the aluminium plate alloys 7050-T7365I, 7010-T7365I and 7010-T765I

The Al-Zn-Mg-Cu alloy 7050 produced by Alcoa is a typical plate and forging alloy because of its low quench sensitivity. In order to compare this alloy with the earlier tested plate alloy 7010 an experimental programme was performed involving tensile, fracture toughness, and fatigue testing. In addition stress corrosion crack initiation and...