Flight simulation environmental fatigue crack propagation in 2024-T3 and 7475-T761 aluminium

Flight simulation fatigue crack propagation tests on 202U-T3 and 7475-T761 aluminum alloy sheet were carried out using a gust spectrum representative of the load history of an under wing skin in a transport aircraft. The investigation included tests at several design stress levels and in environments of laboratory air and air plus water spray....

Environmental effects on crack grwoth in flight-simulation tests on 2024-T3 and 7075-T6 material Supplement: Compilation of test data from an investigation on the effect of environment on crack growth under flight-simulation loading

Flight-simulation tests based on a standardized gust load spectrum were carried out in normal air, very dry air and salt water. Specimen thicknesses were t = 2 mm and t = 10 mm, mean stress in flight was 70 or 55 MN/m². In all cases a significant effect of the environment was found. Fatigue lives for t = 10 ram were much shorter than for t = 2...

Fracture toughness and fatigue properties of the new aluminium alloy 7475-T76

Residual strength tests have been performed on 610 mm wide centre cracked panels. During the tests, stable crack growth was filmed and crack opening displacements were measured. Fracture toughness was determined using the method of Feddersen. Flight simulation fatigue tests were carried out to investigate the crack propagation properties. A...