A test plan for sustained load fracture control verification

An example test plan for sustained load fracture control verification is presented. Two sustained load fracture problems have been chosen: stress corrosion cracking of titanium alloy Ti-6Al-4V, and gaseous hydrogen embrittlement of the nickel-base superalloy Inconel 718. The plan is worked out in detail, including materials and heat treatments,...

Spacecraft sustained load fracture control

The opportunities for sustained load fracture control in spacecraft are indicated. Emphasis is given to verification by small-scale laboratory testing.

Flight simulation fatigue crack propagation in metal/carbon-epoxy laminates

Flight simulation fatigue crack propagation tests with gust spectrum loading were carried out on laminates of (i) aluminium alloy 2024-T3/carbon-epoxy, (ii) aluminium alloy 7475-T761/carbon-epoxy and (iii) titanium alloy Ti-6Al-4V/carbon-epoxy with nominal weight savings of 30% and 40% as compared to equivalent 2024-T3 Alclad and 7475-T761...

Flight simulation fatigue crack propagation in single and double element lugs

Flight simulation fatigue crack propagation tests on single and double element lugs made from 2024-T351 and TOT5-TT351 aluminium alloys and Ti-6AJ.-UV titanium alloy were carried out. Initial damage was a throughthickness notch at one side of each hole in one element. Results showed that crack propagation lives for double element lugs were much...

Review of aeronatical fatigue investigations in the Netherlands during the period march 1977 - february 1979

Paper presented at the 16th ICAP Conference, Brussels, 14 and 15 May 1979.

Comparison of fracture toughness in titanium alloys IMI 550 and IMI 551

Fracture toughness tests on two high strength titanium alloys, IMI 550 and 551, showed that the higher strength alloy, IMI 551, had a much lower toughness. The alloys were very similar in microstructure and fracture mechanisms. A number of model formulations for predicting fracture toughness were compared with the experimental results. This...

Environmental fatigue crack propagation in metal/composite laminates

Flight simulation fatigue crack propagation tests with gust spectrum loading were carried out on 2024-T3/carbon-epoxy, 7475-T76l/carbon-epoxy and Ti-6Al-4V/carbon-epoxy laminates with nominal weight savings of -30% as compared to equivalent 2024-T3 panels. The performance of the 2024-T3/carbon-epoxy laminates was much superior to those of the...

Vacuum fatigue fracture in titanium alloy plate

Environmental fatigue crack propagation in metal/composite laminates: interim report no. 1

Plight simulation fatigue crack propagation tests with gust spectrum loading were carried out on 2024-T3/carbon-epoxy, 7475-T761/carbon-epoxy and Ti-6Al-4V/carbon-epoxy laminates with nominal weight savings of 30% as compared to equivalent 2024-T3 panels. The performance of the 2024-T3/ carbon-epoxy laminates was much superior to those of the...

The influence of texture on environmental fatigue crack propagation in titanium alloys

The effect of sheet thickness on flight simulation fatigue crack propagation in 2024-T3, 7475-T761 and mill annealed Ti-6A1-4V

Flight simulation fatigue crack propagation tests were carried out on 2024-T3, 7475-T761 and mill annealed Ti-6A1-4V sheet in thicknesses up to 3 nim and representative for traJisport aircraft lower wing skin stiffened panels of end load capacities 1.5 and 3 MN/m. There was a significant effect of sheet thickness on crack propagation. Thinner...

Residual strength data of riveted panels with different stiffener configurations

Residual strength tests were carried out on center-cracked panels with a 2024-T3 or 7075-T6 skin and provided with eccentric stiffeners of practical design. The stiffeners were riveted to the skin. The material of the stiffeners was 7075-T6. In some cases the stiffeners were combined with Ti-alloy crack stoppers. On the basis of the test results...

Rate effects on residual strength of flawed structures and materials

The literature is reviewed with respect to: - tests conducted to investigate crack re-initiation under dynamic load and arrest of a running crack - metallurgical sources of rate effects - available data for aerospace engineering materials - mechanical sources of rate effects, i.e. dynamic crack tip stresses and kinetic energy effects Conclusions...