Progressive Damage Accumulation Process of CFRP Cross-Ply Laminates during the Early Fatigue Life

The present work aims at investigating the progressive damage accumulation process of CFRP laminates in an interactive scheme, with a special focus on the early fatigue life where mainly matrix-dominant damage accumulates and stiffness degrades significantly. An in-situ damage monitoring system, containing edge observation, digital image...

Early fatigue damage accumulation of CFRP Cross-Ply laminates considering size and stress level effects

Ply-block size and stress level effect on accumulation of transverse cracks and delamination are investigated during early fatigue life of CFRP laminates. Tension-tension fatigue tests under different stress levels were performed for two cross-ply configurations. Edge observation with digital cameras, digital image correlation and acoustic...