Unfolding the Early Fatigue Damage Accumulation for Cross-ply Laminates

Fatigue damage of composite laminates has attracted considerable attention from research community and industry, in view that laminated structures are inevitable to suffer from fatigue loading during their service life. It is rather complicated to understand and explain, what governs the initiation, accumulation, interaction (synergy or...

Unfolding the early fatigue damage process for CFRP cross-ply laminates

This study investigates the early fatigue damage of cross-ply carbon/epoxy laminates. The aim is to unfold the damage accumulation process, understand the interaction between different damage mechanisms, and quantify their contribution to stiffness degradation. Tension-tension fatigue tests were performed, while edge observation and DIC...