The influence of testing parameters on stress corrosion crack growth in the high strength aluminium alloy 7010-T651

An interlaboratory testing programme to evaluate the rising displacement test for stress corrosion crack (SCO growth investigations was carried out within the framework of the "Measurements and Testing" programme of the European Community under BCR contract nr. MATI CT 930038. The contribution of the NLR to the project consisted of testing of...

Stress corrosion resistance of damage tolerant aluminium-lithium sheet materials

The SCC resistances of three damage tolerant aluminium sheet materials were determined by means of the ASCOR (Automated Stress COrrosion Ring) test. The conventional damage tolerant sheet material 2024-T3 was used as reference. The SCC resistance of 8090-T81 turned out to be only slightly lower than the SCC resistance of 2024-T3. In contrast,...

Outdoor corrosion testing of aluminium-lithium alloys

Outdoor corrosion and stress corrosion tests were conducted on Al-Li plate and sheet materials for 3 and almost 5 years respectively. The results can be summarized as follows: Corrosion: Peak aged XXXA-T651 (8090-T651) exhibited greater exfoliation corrosion resistance than 2024-T351 and 2324-T39 plate. 2091-T3 and 2024-T3 sheet were found to be...