The retrogression and re-aging (RRA) processes, aimed mainly at tailoring intergranular precipitates, could significantly improve the corrosion resistance (i.e., stress corrosion cracking resistance) without considerably decreasing the strength, which signifies that an efficient control of the size, distribution and evolution of intergranular...

Effect of Main Elements (Zn, Mg, and Cu) on Hot Tearing Susceptibility During Direct-Chill Casting of 7xxx Aluminum Alloys

New 7xxx aluminum alloys with high alloying contents are being designed, which could induce serious hot tearing defects during direct-chill (DC) casting. Among all factors affecting hot tearing of 7xxx alloys, undoubtedly alloying elements play a significant role. In this study, the effect of main alloying elements (Zn, Mg, and Cu) on hot...