Evaluation of the Non-destructive Character of the Stiffness Damage Test for Damage Assessment of Concrete Structures Affected by Alkali-Silica Reaction Using Acoustic Emission

The Stiffness Damage Test (SDT), a cyclic test in compression, is considered as a reliable tool for assessing concrete structures affected by ASR. Depending on the extent of ASR damage in concrete, loading levels up to 40% of the compressive strength may contribute to increasing internal damage during testing. Nevertheless, previous research...

Can superabsorbent polymers be used as rheology modifiers for cementitious materials in the context of 3D concrete printing?

Autogenous shrinkage may be a critical issue concerning the use of limestone-calcined clay-cement (LC3) in high-performance concrete and 3D printable cementitious materials, which have relatively low water to binder (W/B) ratio. Adding an internal curing agent, i.e., superabsorbent polymer (SAP), could be a viable solution in this context....

Fresh properties of limestone-calcined clay-slag cement pastes

Formulation of quaternary blended system containing ordinary Portland cement or clinker, slag, limestone and calcined clay (LC2) appeared to be a viable approach to developing low-clinker cements without severely sacrificing mechanical performance at later ages. This paper investigates the effect of two material parameters, i.e., LC2-to-slag...

Effect of curing methods during a long time gap between two printing sessions on the interlayer bonding of 3D printed cementitious materials

A good bond between the layers of 3D printed cementitious materials is a prerequisite for having high structural rigidity for the printed elements. However, the influence of printing process on an interlayer bond is still not well understood. This study investigates the influence of curing methods (i.e., air curing, plastic film covering, wet...

A study of the elastic moduli and chemical composition of corrosion product naturally-generated due to chlorides through nano-indentation and energy dispersive X-ray spectrometry (EDS)

An important input parameter for numerical models that simulate cracking of the concrete cover due to reinforcement corrosion is the Elastic modulus of corrosion product (Ecp). Despite its relevance, Ecp is subject of significant variations according to the values reported in the literature, which vary from less than 100 MPa up to 360 GPa....

Analysis of naturally-generated corrosion products due to chlorides in 20-year old reinforced concrete: An elastic modulus-mineralogy characterization

The elastic modulus of corrosion product (E_cp) has been reported with significant variations in the literature. This study aims to investigate the E_cp of naturally-generated chloride-induced corrosion products formed in different concrete mixes. Microstructural characterization was conducted through nano-indentation,...

Determination of loss of reinforcement due to corrosion through X-ray computer micro-tomography

X-ray computer scanning tomography (CT scan) is an increasingly more available technique, which has been applied to material sciences for years. Although most of its use is qualitative for gaining insights on material behavior, quantitative analysis for estimations of deterioration rates is possible. This paper describes an unbiased,...

The influence of defects at the steel/concrete interface for chloride-induced pitting corrosion of naturally-deteriorated 20-years-old specimens studied through X-ray Computed Tomography

Although reinforcement corrosion is a well-known issue, which are the locations of the steel/concrete interface most sensitive to pitting corrosion is still an unclear issue. In this study, X-ray computed tomography is used to characterize eight 20-years-old reinforced concrete cores naturally deteriorated due to chloride-induced corrosion....

The influence of defects at the steel/concrete interface for pitting corrosion initiation studied through X-ray Computed Tomography and image analysis

Although corrosion of reinforcement is a well-known issue for the construction industry, there are still open questions about some fundamentals of corrosion in reinforced concrete. These points include, among others, which are the most sensitive locations of the steel/concrete interface for pitting corrosion to initiate and to propagate. In...

Piezoresistive properties of cementitious composites reinforced by PVA fibres

The use of fibres to enhance the ductility of cementitious composites has been extensively studied for the past few years. The addition of polymeric or metalic fibres with random orientation to the composite or even natural long and aligned fibres demonstrated a very successful reinforcement capable to reach a high mechanical performance....