Impact of the Current on Reverse Bias Degradation of Perovskite Solar Cells

Nonequal current generation in the cells of a photovoltaic module, e.g., due to partial shading, leads to operation in reverse bias. This quickly causes a significant efficiency loss in perovskite solar cells. We report a more quantitative investigation of the reverse bias degradation. Various small reverse biases (negative voltages) were...

Fundamental Mechanisms Behind the Reverse Characteristic of Cu(In,Ga)Se₂ Solar Cells

Partial shading of PV modules can lead to degradation of the shaded cells. The degradation originates from a reverse bias voltage over the shaded cells. In order to mitigate reverse bias damage in Cu(In, Ga)Se2 (CIGS) modules, a good understanding of the fundamental mechanisms governing the reverse characteristic is required. In this study, a...

Determining the decomposition voltage of Cu(In_1-xGa_x)Se₂

Partial shading of CIGS modules can lead to permanent damage of the module in the shaded area. This is caused by harmful reverse bias voltages in the shaded area which lead to reverse bias induced defects, also known as wormlike defects. A lot is already known about the origin and propagation of wormlike defects. However, the fundamental...