Fundamental Mechanisms Behind the Reverse Characteristic of Cu(In,Ga)Se₂ Solar Cells

Partial shading of PV modules can lead to degradation of the shaded cells. The degradation originates from a reverse bias voltage over the shaded cells. In order to mitigate reverse bias damage in Cu(In, Ga)Se2 (CIGS) modules, a good understanding of the fundamental mechanisms governing the reverse characteristic is required. In this study, a...

Determining the decomposition voltage of Cu(In_1-xGa_x)Se₂

Partial shading of CIGS modules can lead to permanent damage of the module in the shaded area. This is caused by harmful reverse bias voltages in the shaded area which lead to reverse bias induced defects, also known as wormlike defects. A lot is already known about the origin and propagation of wormlike defects. However, the fundamental...

Propagation mechanism of reverse bias induced defects in Cu(In,Ga)Se₂ solar cells

Partial shading of monolithically interconnected Cu(In,Ga)Se₂ (CIGSe) modules can lead to the formation of reverse bias induced defects. These localized defects permanently reduce the output of the PV module. The formation and propagation mechanisms of these defects is studied. Understanding these mechanisms can help to prevent or...

Material Property Changes in Defects Caused by Reverse Bias Exposure of CIGS Solar Cells

Partial shading of Cu(In,Ga)Se₂ modules can lead to the formation of reverse bias induced wormlike defects. These wormlike defects act as local shunts and permanently decrease module output. A good understanding of the formation and propagation mechanisms of these defects is needed in order to mitigate the negative effects, or to...