Effect of corrosion on the fatigue service-life on steel and reinforced concrete beams

Chloride-induced corrosion is a point of big concern in reinforced concrete (RC) structures. To monitor the actual health and to predict the remaining service-life of structures, it is important to understand the structural behaviour and the failure mechanism of structures exposed to chlorides under fatigue loading conditions. A beam test,...

Dynamically loaded beam failure under corroded conditions

De-icing salts, used on roads in heavy winters, may enter reinforced concrete (RC) structures via its capillary pore system or via cracks, initiating reinforcement corrosion and reducing its remaining service-life. Vehicles passing real bridges exert a dynamic impact action that might activate a fatigue failure mechanism. In order to generate...

Automatic Degradation Detection During a Dynamic Loaded Beam Test

The remaining service life of concrete structures strongly depends on the corrosion level of the reinforcement bars. It explains that measuring the corrosion rate is a key issue in monitoring the structural health of concrete structures. A common and appropriate technique used to evaluate the instantaneous corrosion rate of steel reinforcement...

Structural monitoring and modal properties of a real time bridge and lab tests

For understanding the actual state of durability of concrete structures, it is important to know its response due to external loading. This response mainly depends on the actual structural and material properties of the structure, while loaded. Mechanical and chemical degradation are the main mechanisms that may affect these properties with time...

Polymeric nano-materials for corrosion control of steel in concrete

Polymeric nano-materials utilization in reinforced concrete, aiming to deal with steel corrosion was developed in previous works. Promising results were obtained with PEO–b–PS nano-formations, both in terms of enhanced bulk matrix properties and improved steel corrosion resistance. Recent research has been focusing on a cheaper and commercially...

Service life and life cycle cost modelling of cathodic protection systems for concrete structures

Corrosion of reinforcing steel in concrete structures causes concrete cracking, steel diameter reduction and eventually loss of safety. In infrastructure this is mainly due to penetration of chloride ions from de-icing or marine salts. Conventional repair means heavy, labour intensive and costly work and economic pressures (time and money) work...