Experimental parametric investigation on the behavior of adhesively bonded CFRP/steel joints

This paper presents an extensive experimental and numerical study on the behavior of CFRP/Steel adhesively bonded double strap joints (DSJ). A total of 50 DSJ specimens were tested under static tensile loading. The digital image correlation (DIC) was used to measure the backface deformation. A total of six adhesives that feature different...

High performance and cost-effective hybrid steel/CFRP joints using bi-adhesive technique for the repair of metallic infrastructures

The use of the brittle adhesives commonly adopted in construction industry do not provide the best performance for steel structures. CFRP/Steel joint bonded with extremely tough adhesive achieve much higher strength and ductility. However, tough adhesives are not developed for the construction industry and their cost may question the...

Novel adherend laminate designs for composite bonded joints

Adhesive bonding is one of the most suitable joining technologies in terms of weight and mechanical performance for current carbon fiber reinforced polymer aircraft fuselage structures. However, traditional joint topologies such as single overlap joints induce high peel stresses, resulting in sudden failure and low joint strength when compared...

Effect of moisture on the adhesion of CFRP-to-steel bonded joints using peel tests

In this work, an experimental study has been carried out to evaluate the effect of salt water condition on the long-term adhesion of composite-to-metal bonded joints using peel tests. A new test configuration is tested via fully and partially immersed specimens with 500 mm length. Fracture surfaces of non-aged samples exhibited a cohesive...

Interlaminar adhesion assessment of carbon-epoxy laminates under salt water ageing using peel tests

The aim of this study is to assess the interlaminar adhesion of carbon-epoxy laminates under salt water condition. Carbon-epoxy laminate specimens were immersed in a salt water tank for 60 days. Some specimens were then dried at<br/>room temperature for 280 days, until recovering their initial weight. Specimens were tested using the composite...

Adhesion quality of steel-CFRP interface bonding

In this work, peel tests were used to assess the adhesion quality between carbon fiber reinforced polymers (CFRP) and carbon steel plates. The tests were performed according to the ASTM standard of floating roller peel tests (D3167–97) with a new specimen layup. The layup and geometry of specimens was defined in order to have the CFRP as the...