- document
-
Schra, L. (author), 't Hart, W.G.J. (author)Long-term outdoor stress corrosion tests were executed on overaged 7000 series aluminium alloy plate and forgings. Plate material of the alloys 7010-T7651, 7010-T7451 and 7075-T7351 exhibited an excellent resistance to SCC. PM alloy X7091-T7E69 forgings combined a higher strength with superior SCC resistance as compared to IM alloy forgings. The...report 1988
- document
-
Wanhill, R.J.H. (author), Schra, L. (author)Constant amplitude low stress Intensity fatigue crack growth for 2024-T3 and 7475-T761 aluminium alloys In laboratory air, sump tank water and synthetic seawater was Investigated. Corrosion fatigue crack grouwt retardation and arrest occurred In both sump tank water and synthetic seawater, resulting In higher AKth values than In air. Crack...report 1987
- document
-
Kolkman, H.J. (author)The effect of penetrant on the fatigue life of single shear riveted lap joints was investigated by flight simulation fatigue tests using the MINITWIST gust spectrum. The penetrant/material combination investigated was ARDROX 985 P3T and aluminium alloy 202U-T3 sheet material (both bare and clad) respectively. The effect of penetrant on the...report 1982
- document
-
Schra, L. (author), Faber, J. (author)An experimental investigation was carried out into the applicability of various corrosive environments for stress corrosion crack propagation testing of high strength aluminium alloys using double cantilever beam specimens. Testing under atmospheric conditions was used as a reference. It was found that stress corrosion crack growth under...report 1981
- document
-
Nederveen, A. (author), de Jong, J.B. (author)The influence of the approximation of the lower end of the load spectrum was investigated by comparative tests using the Basic F-27 test programme and an extended version, containing three times more cycles per flight. Crack growth was studied on notched sheet specimens made of Alclad 202U-T3 and Alclad TOT5-T6. Fatigue life tests were done on...report 1981