Uncovering the white etching area and crack formation mechanism in bearing steel

The microstructure of a damaged bearing from the field was characterized in this work with the intention to better understand microstructural features behind formation of White Etching Cracks (WEC) in bearings. Microstructural characterization of the altered white etching area (WEA) involved conventional electron backscattered diffraction ...

In situ study on fracture behaviour of white etching layers formed on rails

Failure in engineering materials like steels is strongly affected by in-service deleterious alterations in their microstructure. White Etching Layers (WELs) are an example of such in-service alterations in the pearlitic microstructure at the rail surface. Cracks initiate in the rails due to delamination and fracture of these layers and...