Static and fatigue strength of an adhesive bonded CFRP butt-strap joint, the effects of stacking sequence and temperature

Fatigue damage in composites under different loading conditions

The damage development In notched (± 45, 0„, 90, 0-) carbon-epoxy coupon specimens tested under different loading conditions was determined. Constant amplitude tests at R = -1 and R = 0.1 as well as flight simulation tests were performed to establish those stress values for which no damage growth occurs.

An investigation of crack resistance in composite reinforced face sheets of sandwich panels

Aluminium sandwich paaiels provided with carbon-epoxy uniaxial reinforcing strips were fatigued and subsequently tested for residual strength, Although both analysis ajid fatigue tests indicate that the crack tip zone is affected onlywhen the zone is in the immediate vicinity of a stiffener the reinforcement considerably increases crack...