Long-term outdoor stress corrosion testing of overaged 7000 series aluminium alloys

Long-term outdoor stress corrosion tests were executed on overaged 7000 series aluminium alloy plate and forgings. Plate material of the alloys 7010-T7651, 7010-T7451 and 7075-T7351 exhibited an excellent resistance to SCC. PM alloy X7091-T7E69 forgings combined a higher strength with superior SCC resistance as compared to IM alloy forgings. The...

Fracture toughness and corrosion properties of the aluminium plate alloys 7010-T651 and 7150-T6E189

A comparative experimental investigation was done on the advanced plate alloys 7010-T651 from ALCAN and 7150-T6E189 from ALCOA. The mechanical properties, fracture toughness and corrosion properties were determined. The most notable finding was the excellent fracture toughness of alloy 7150-T6E189 combined with a high tensile strength. The...

Effect of cooling rate on corrosion properties and microstructure of high strength aluminium alloys

The Jominy end-quench test was applied to rods of the alximinium alloys T010 and X TO9I to obtain a decreasing cooling rate over the length of the rods. After heat treating to a high strength T6 and an overaged TT condition the corrosion properties and the microstructure were determined related to the cooling rate. No influence of cooling rate...

Engineering property comparisons of PM alloy X7091-T7E69 and IM alloy forgings

The engineering properties of PM alloy X7091-T7E69 forgings were compared with those of forgings of the IM alloys 7075-T73, 7175-T736, 7050-T736 and 7010-T736. The properties considered were: strength, fracture toughness, fatigue crack propagation under constant amplitude and flight simulation loading, stress corrosion crack initiation and...

Influence of environments on constant displacement stress corrosion crack growth in high strength aluminium alloys

An experimental investigation was carried out into the applicability of various corrosive environments for stress corrosion crack propagation testing of high strength aluminium alloys using double cantilever beam specimens. Testing under atmospheric conditions was used as a reference. It was found that stress corrosion crack growth under...

The effect of sheet thickness and laminating on the fatigue resistance of the aluminium alloyd AL-7010T73651

The influence of sheet thickness (2 mm and 10 mm) and the influence of laminating (5x2 ram) on the fatigue crack growth properties of the aluminium alloy AL 7010-T 73651 were investigated. Both constant amplitude loading and flight simulation loading were applied. All 2 mm and 10 mm thick sheets were machined from a 150 mm thick plate, i.e....

The Jominy end-quench test for investigation of corrosion properties and microstructure of high strength aluminium alloys

The Jominy end-quench test was applied to extruded rods of the aluminium alloys 2024 and 7075 to obtain a decreasing quench rate over the length of the rods. Subsequently the alloys were heat treated to the conditions: 2024-T4, 2024-T6, 7075-T73. A corrosion investigation and a transmission electron microscopy investigation were performed to...