Aircraft corrosion and fatigue damage assessment (USAF ASIP Publication)

This paper reviews currently available information on corrosion and fatigue in aircraft as a background to discussing the assessment of corrosion and fatigue damage. The main topics are: - aircraft operating environments and loads - corrosion - fatigue - corrosion and fatigue - corrosion and fatigue damage assessment. Aircraft structures are...

Flight simulation environmental fatigue crack propagation in 2024-T3 and 7475-T761 aluminium

Flight simulation fatigue crack propagation tests on 202U-T3 and 7475-T761 aluminum alloy sheet were carried out using a gust spectrum representative of the load history of an under wing skin in a transport aircraft. The investigation included tests at several design stress levels and in environments of laboratory air and air plus water spray....

Review of aeronatical fatigue investigations in the Netherlands during the period march 1977 - february 1979

Paper presented at the 16th ICAP Conference, Brussels, 14 and 15 May 1979.

Evaluation of non-destructive inspection methods applied to milled step-down areas

The present report describes how fatigue cracks were produced in 102 specimens. After cracking these specimens were inspected non-destructively by means of eddy currents, ultrasonics. X-rays and penetrants, and the indications were recorded. Successively the specimens were exposed to corrosion whereafter the inspections were repeated. Upon...

Breukvlakonderzoek

In this report an attempt is made to give an overview of the various aspects involved in a fracture surface investigation, stating with a definition of fractography and why it is done. Then the equipment needed is discussed, including stereo-microscopes, optical microscopes, transmission and scanning electron microscopes, and micro-analysis...

Aluminium alloys for advanced structural applications in transport aircraft

This paper concisely reviews and discusses (1) metallurgically cleaner alloys like -2124, 2048 and 7475, (2) potential application of 7000 series alloys in tension panels, (3) development of high strength stress corrosion resistant thick section materials like 7010, 7049 and 705O, (4) powder metallurgy 7000 series alloys with high strength and...