Constant-amplitude and flight-simulation fatigue tests on adhesive bonded lap joint specimens of 2024-T3 sheet material

Fatigue tests were carried out on Redux and FM 123/5 bonded specimens at various stress levels, temperatures (RT to 65 C) and low and high test frequencies. Observations were made on the type of failure (bond line failure or sheet failure) and the significance of the adhesive squeezeout for crack nucleation. An analysis of the data and a...

Some tests to assess the effect of crack stoppers on the fatigue life of centre-notched sheetspecimens

Several simple crack stopping methods were evaluated In fatigue crack propagation tests on 2024-T3 Alclad sheet specimens. After precracklng until a crack of 40 mm was obtained crack stoppers were Installed and the fatigue test was continued. Crack stoppers Installed In stop holes were: a blind rivet, a hard driven rivet, a heavily tightened...

Review of aeronatical fatigue investigations in the Netherlands during the period march 1977 - february 1979

Paper presented at the 16th ICAP Conference, Brussels, 14 and 15 May 1979.

Effect of an anti-corrosion penetrant on the fatigue life in flight-simulation tests on various riveted joints

Comparative flight-simulation tests on four types of joints of 2024- T3 sheet material were carried out with and without application of the penetrant LPS-3. Types of joints were douhle strap joint with hi-lok bolts, asymmetric strap joint, lap joint with countersunk rivets and lap joint with dimpled holes. Observations on slip during the fatigue...

The effect of sheet edge working on the fatigue life under flight-simulation loading

Fatigue tests under flight-simulation loading have been performed on unnotched Alclad 2024-T3, anodised 2.0 mm thick sheet specimens, manufactured according to several machine-shop processes applied in the air craft industry. From the results it appears that milling is preferable to stamping. Rounding off the edges is also advantageous. The...

Environmental effects on crack grwoth in flight-simulation tests on 2024-T3 and 7075-T6 material Supplement: Compilation of test data from an investigation on the effect of environment on crack growth under flight-simulation loading

Flight-simulation tests based on a standardized gust load spectrum were carried out in normal air, very dry air and salt water. Specimen thicknesses were t = 2 mm and t = 10 mm, mean stress in flight was 70 or 55 MN/m². In all cases a significant effect of the environment was found. Fatigue lives for t = 10 ram were much shorter than for t = 2...

The significance of cladding for fatigue of aluminium alloys in aircraft structures

Flight-simulation tests were carried out on sheet specimens notched "by an open hole (Kt = 2.66). The material was 2024-T3 in three conditions; Alclad, bare and chemically milled. The crack initiation period and the crack propagation period were considerably shorter for the Alclad material. The significance of the cladding, both for constant...

Flight-simulation tests on notched elements

Tests were carried out on open-hole specimens, lugs and riveted strap joints of 2024-T3 and 7075-T6 materials. The effects of design stress level, truncating high-amplitude gust loads and omitting low-amplitude gust cycles were stuaied. Observations of the open-hole specimens include data on crack initiation, crack closure and damage increments....