Analysis of naturally-generated corrosion products due to chlorides in 20-year old reinforced concrete: An elastic modulus-mineralogy characterization

The elastic modulus of corrosion product (E_cp) has been reported with significant variations in the literature. This study aims to investigate the E_cp of naturally-generated chloride-induced corrosion products formed in different concrete mixes. Microstructural characterization was conducted through nano-indentation,...

The influence of defects at the steel/concrete interface for chloride-induced pitting corrosion of naturally-deteriorated 20-years-old specimens studied through X-ray Computed Tomography

Although reinforcement corrosion is a well-known issue, which are the locations of the steel/concrete interface most sensitive to pitting corrosion is still an unclear issue. In this study, X-ray computed tomography is used to characterize eight 20-years-old reinforced concrete cores naturally deteriorated due to chloride-induced corrosion....

The effect of the steel–concrete interface on chloride-induced corrosion initiation in concrete: a critical review by RILEM TC 262-SCI

The steel–concrete interface (SCI) is known to influence corrosion of steel in concrete. However, due to the numerous factors affecting the SCI—including steel properties, concrete properties, execution, and exposure conditions—it remains unclear which factors have the most dominant impact on the susceptibility of reinforced concrete to...

The steel–concrete interface

Although the steel–concrete interface (SCI) is widely recognized to influence the durability of reinforced concrete, a systematic overview and detailed documentation of the various aspects of the SCI are lacking. In this paper, we compiled a comprehensive list of possible local characteristics at the SCI and reviewed available information...

Incorporating cracking of concrete on chloride ingress and service life modeling of concrete structures

Chloride induced reinforcement corrosion is the most common degradation mechanisms for reinforced concrete structures. The service life of concrete structures is normally predicted by estimating the rate of chloride ingress and the necessary time to initiate reinforcement corrosion. Normally, chloride ingress is modeled as a diffusive process in...