- document
-
Schijve, J. (author), Jacobs, F.A. (author)Fatigue tests were carried out on Redux and FM 123/5 bonded specimens at various stress levels, temperatures (RT to 65 C) and low and high test frequencies. Observations were made on the type of failure (bond line failure or sheet failure) and the significance of the adhesive squeezeout for crack nucleation. An analysis of the data and a...report 1984
- document
-
de Jonge, J.B. (author), Nederveen, A. (author), Tromp, P.J. (author)Riveted specimens that are considered representative for F-27 type wing structure were subjected to comparative flight simululation test in which the gust load severity and Ground-Air-Ground cycle were systematically varied. The effect of these variations on crack propagation behaviour was studied by means of crack growth tests on 2 mm sheet...report 1978
- document
-
de Jonge, J.B. (author), Nederveen, A. (author), Tromp, P.J. (author)Fatigue tests under flight simulation loading were done on simple notched 2024-T3 Alclad sheet specimens. Reduction of the gust load amplitudes resulted in an increase of crack initiation life but hardly influenced crack propagation. Reduction of the overall stress level increased both initiation and crack propagation life. The observed...report 1978
- document
-
Schra, L. (author), van Leeuwen, H.P. (author)The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...report 1977
- document
-
Wanhill, R.J.H. (author), Schra, L. (author)The effects of flat to slant fracture transitions on flight simulation fatigue crack propagation in specimens of 7O5O aluminium alloy forgings are discussed. For specimens containing flat, shearlipped, or full slant fractures at similar crack lengths the crack resistance (R curve) approach appears to provide an explanation for differences in the...report 1976
- document
-
Schra, L. (author), van Leeuwen, H.P. (author), Meulman, A.E. (author)The fatigue crack propagation performance of the alloy AZ 74.61 under manoeuvre spectrum loading was studied. The crack propagation behaviour was also compared with that of the American forging alloy AA 7050, not only for simulated manoeuvre loading but also for simulated gust loading and programme loading. It was found that, at comparable...report 1976
- document
-
Schra, L. (author), van Leeuwen, H.P. (author)The effect of variety of heat treatments on various engineering properties was studied with the aim to derive an optimum heat treatment. The engineering properties comprised Vickers hardness, short-time tensile strength, fatigue crack propagation resistance, fracture toughness and stress corrosion resistance. The test results were compared with...report 1976
- document
-
't Hart, W.G.J. (author), Nederveen, A. (author), Stoffels, E. (author), Tromp, J. (author)Residual strength tests have been performed on 610 mm wide centre cracked panels. During the tests, stable crack growth was filmed and crack opening displacements were measured. Fracture toughness was determined using the method of Feddersen. Flight simulation fatigue tests were carried out to investigate the crack propagation properties. A...report 1975