This work presents an investigation of the microstructure development during the application of the quenching and partitioning (Q&P) process to two stainless steels with different Mn content. The results are compared with calculations based on the constrained carbon equilibrium theory, paying special attention to the presence of reactions competing for the carbon available for partitioning and to the effect of alloying element segregation. Results show that chromium carbides must be considered when accounting for the carbon available for austenite stabilisation. Moreover, manganese/chromium segregation bands play an important role in the microstructure development, particularly in martensite formation, with important consequences in the microstructure development during the following processing steps.

The present article investigates the influence of chemical composition and phase fractions on the corrosion behaviour of industrially produced quenching and partitioning (Q&P) martensitic stainless steels. Localised corrosion was analysed by scanning Kelvin probe force microscopy (SKPFM) and scanning electrochemical microscopy (SECM) in 3.5 wt.% NaCl solution. SKPFM revealed a Volta-potential difference of around 40 mV between inclusions and the matrix, which is larger than the Volta potential variations within the matrix. This difference in surface potential is a driving force for selective dissolution (corrosion initiation) at inclusions and inclusion/matrix interfaces. SECM detected early pitting initiation, particularly in alloys containing MnS and TiN inclusions. Results suggest that pitting initiation and propagation occur at those specific regions. This study emphasised that irrespective of chemical composition and phase fraction, localised corrosion initiation in Q&P-processed martensitic stainless steels is predominantly governed by the presence of inclusions.

Quenching and partitioning (Q&P) treatment has been proven effective in manufacturing advanced high strength steels with high content of retained austenite, showing the improved balance of high strength and sufficient ductility. This method has been very well elaborated for carbon steel processing over the last two decades. Though it can also be potentially applied for processing other steel families, this has been scarcely studied. This article focuses on the effect of chemistry and heat treatment parameters on the microstructure and properties of Q&P treated martensitic stainless steels. Three different martensitic stainless steels with different contents of alloying elements are subjected to Q&P processing with varying quenching temperature or partitioning temperature and partitioning time. The tensile behavior of the Q&P treated steels is studied. The effect of chemistry and Q&P treatment parameters on the microstructure and tensile properties is analyzed. The effect of plastic deformation on the microstructure of the Q&P treated steels is also investigated. It is demonstrated that the Q&P treated martensitic stainless steels can show a good combination of enhanced strength and sufficient tensile ductility. Their uniform elongation increases with the increasing volume fraction of retained austenite due to the transformation induced plasticity (TRIP) effect. The ability of the martensitic matrix to accumulate plastic deformation also plays an important role. The Q&P process - microstructure - property relationship is discussed.

Recent studies have demonstrated the viability of quenching and partitioning (Q&P) treatment for processing martensitic stainless steels showing an improved balance of high strength and sufficient ductility. However, to date, the fatigue behaviour of these materials has not been explored. This study examines the effect of their complex hierarchic microstructure on high cycle fatigue performance. Three steels with different alloying element contents underwent Q&P processing, resulting in multiphase microstructures rich in retained austenite. High cycle fatigue tests and analysis of fatigue fracture surfaces were performed using SEM and EBSD techniques. The results indicate satisfactory high cycle fatigue performance in Q&P treated martensitic stainless steels, surpassing traditional counterparts. Fatigue cracks predominantly form and propagate along martensite packet and block boundaries, while prior austenite grain boundaries and MnS inclusions have minimal influence on fatigue crack formation and growth. Microplastic deformation at the fatigue crack tip enhances local KAM values and triggers localized transformation of retained austenite grains. It is hypothesized that the developed Q&P treated martensitic stainless steels exhibit improved resistance to low cycle fatigue.