Exploring the effect of complex hierarchic microstructure of quenched and partitioned martensitic stainless steels on their high cycle fatigue behaviour

Journal Article (2023)
Author(s)

A. Sierra Soraluce (IMDEA Materials Institute)

G. Li (TU Delft - Team Maria Santofimia Navarro)

Maria Jesus Santofimia Navarro (TU Delft - Team Maria Santofimia Navarro)

J. M. Molina-Aldareguia (IMDEA Materials Institute, Universidad Politécnica de Madrid)

A. Smith (Rina Consulting - Centro Sviluppo Materiali)

Marta Muratori (Acerinox Europa SAU)

I Sabirov (IMDEA Materials Institute)

Research Group
Team Maria Santofimia Navarro
Copyright
© 2023 A. Sierra Soraluce, G. Li, Maria Jesus Santofimia, J. M. Molina-Aldareguia, A. Smith, M. Muratori, I. Sabirov
DOI related publication
https://doi.org/10.1016/j.matdes.2023.112286
More Info
expand_more
Publication Year
2023
Language
English
Copyright
© 2023 A. Sierra Soraluce, G. Li, Maria Jesus Santofimia, J. M. Molina-Aldareguia, A. Smith, M. Muratori, I. Sabirov
Research Group
Team Maria Santofimia Navarro
Volume number
233
Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Abstract

Recent studies have demonstrated the viability of quenching and partitioning (Q&P) treatment for processing martensitic stainless steels showing an improved balance of high strength and sufficient ductility. However, to date, the fatigue behaviour of these materials has not been explored. This study examines the effect of their complex hierarchic microstructure on high cycle fatigue performance. Three steels with different alloying element contents underwent Q&P processing, resulting in multiphase microstructures rich in retained austenite. High cycle fatigue tests and analysis of fatigue fracture surfaces were performed using SEM and EBSD techniques. The results indicate satisfactory high cycle fatigue performance in Q&P treated martensitic stainless steels, surpassing traditional counterparts. Fatigue cracks predominantly form and propagate along martensite packet and block boundaries, while prior austenite grain boundaries and MnS inclusions have minimal influence on fatigue crack formation and growth. Microplastic deformation at the fatigue crack tip enhances local KAM values and triggers localized transformation of retained austenite grains. It is hypothesized that the developed Q&P treated martensitic stainless steels exhibit improved resistance to low cycle fatigue.