To achieve an effective design of additively manufacturable Ni superalloys with decent service performance, a hybrid computational design model has been developed, where the strategy to tailor local elemental segregations was integrated within a scheme of minimizing the cracking susceptibility. More specifically, the phase boundary of primary NbC / γ matrix was introduced into the design routine to tune the spatial distribution of critical solutes at an atomic scale, thereby inhibiting the formation of borides and segregation-induced cracking. Based on the output of the design, new grades of Ni superalloy have been developed with excellent additive manufacturability, as confirmed by the robustness of printing parameters in fabricating low-defect-density samples. The capability of the phase boundaries to evenly distribute boron atoms was validated experimentally, and the cracking induced by uncontrolled boron segregation at grain boundaries was effectively prevented. The newly designed alloys showed good tensile properties and decent oxidation resistance at different service temperatures, which are comparable to those of conventionally produced superalloys. The finding that phase boundaries can be employed to prevent undesirable clustering of boron atoms can be extended to manipulate the distributions of other critical elements, which provides a new path for designing novel Ni superalloys with balanced printability and mechanical properties.@en

Herein, the effect of Nb content on the phase transformation kinetics, microstructure, and mechanical properties of hot-rolled quenching and partitioning (Q&P) steel is investigated. The characteristics of three C–Mn–Si–Ti steels (0.18C, 2.0Si, 2.6Mn, and 0.015Ti) containing 0, 0.027, or 0.061 wt% Nb are compared. Results reveal that grain boundary pinning by precipitates and Nb solute drag effects refine the austenite grain size during the hot-rolling process; the microstructural refinement is carried over to the final microstructure subjected to the Q&P treatment. The remaining supersaturated Nb suppresses the bainite formation and decreases the final bainite fraction formed in the Q&P process. The microstructural evolution leads to an increase in the ultimate tensile strength (UTS) of the steel containing 0.027 wt% Nb from 1169 to 1228 MPa, while keeping the total elongation at 18%. When the Nb content is increased to 0.061 wt%, the UTS of the steel increases to 1313 MPa, but the elongation at break drops to 16%. The effect is due to the carbon consumption by the Nb precipitates, which causes a decrease in the stability of the retained austenite and reduces the strain hardening at high strain levels.@en